This study investigates the effect of the diethyl carbonate as a carbonation accelerator on the carbonation of lime mortars. Two types of lime mortars were prepared, one using lime putty and standard sand and the other using lime putty, dust and fragments of ceramic and standard sand. After a curing time of two weeks, the accelerator product, diethyl carbonate in a solution of ethanol and water, was sprayed on half of the mortars of each type. The differences in the carbonation performance were analyzed at 28, 90, 120 and 180 days using different analytical methods. Apart from the mineralogical and petrographic characterization, the physical, mechanical and hydric properties of the samples were determined. Mechanical tests were conducted only at 90, 120 and 180 days, because at 28 days the lime mortars were considered still too soft. The mortar samples with the accelerator had steadier carbonation and slight changes in their microstructure.

Calcareous materials such as limestone and lime-based mortars, widely used in the Built Heritage, are often subjected to degradation processes that can lead to loss of cohesion and material loss. Consolidation of these materials with liquid products via the surface is a common practice; however, the most used consolidation products (e. g. TEOS-based) show a poor physical-chemical compatibility with calcareous substrates. For application on calcareous materials, the so-called nanolimes, i. e. dispersions of lime nanoparticles in alcohols, are an alternative to TEOS-based products, thanks to their chemical compatibility with lime-based substrates. Nanolimes can help to recover a superficial loss of cohesion. However, their in-depth consolidation effect is not always satisfactory. Previous work has shown that a better deposition of lime nanoparticles in depth can be achieved by adapting the properties of the nanolime dispersion (kinetic stability and evaporation rate) to the moisture transport properties of the substrate, through optimization of the solvent. In this paper, freshly synthetized nanolimes were dispersed in pure ethanol and/or in binary mixture of ethanol (95 %) and water (5 %). These nanolimes were applied on Maastricht limestone and on a lime-based mortar by capillary absorption (method commonly used for laboratory tests) and by nebulization (method widely used in situ). The aim of this research is to fill the gap between laboratory tests and on site application, providing an application protocol for restorers and professionals in the field. The research shows that results obtained by application by capillary absorption do not always correspond to those obtained by nebulization. This fact should be considered when deciding on the use of a consolidation surface treatment in practice.

Several concrete structures had shown signs of degradation some years after construction due to internal expansive reactions. Among these reactions there are the alkaliaggregate reactions (AAR) that occur between the aggregates and the concrete interstitial fluids which can be divided in two types: the alkali-silica reaction (ASR) and alkali-carbonate reaction (ACR). The more common is the ASR which occurs when certain types of reactive silica are present in the aggregates. In consequence, an expansive alkali-silica gel is formed leading to the concrete cracking and degradation. Granites are rocks composed essentially of quartz, micas and feldspars, the latter being the minerals which contain more alkalis in their structure and thus, able to release them in conditions of high alkalinity. Although these aggregates are of slow reaction, some structures where they were applied show evidence of deterioration due to ASR some years or decades after the construction. In the present work, the possible contribution of granitic aggregates to the interstitial fluids of concrete by alkalis release was studied by performing chemical attack with NaOH and KOH solutions. Due to the heterogeneity of the quarries in what concerns the degree of alteration and/or fracturing, rock samples with different alteration were analysed. The alteration degree was characterized both under optical microscope and image analysis and compared with the results obtained from the chemical tests. It was concluded that natural alteration reduces dramatically the releasable alkalis available in the rocks.

Pese embora o esforço realizado nos últimos anos, a nível internacional e nacional, para a melhoria do comportamento do betão e na prevenção da sua degradação, continua-se a assistir ainda ao aparecimento dum número elevado de estruturas de betão com problemas de durabilidade, essencialmente os relacionados com causas químicas, como são exemplo as reações expansivas internas e a corrosão das armaduras. Neste contexto, o correto diagnóstico da(s) forma(s) de degradação presentes numa determinada estrutura de betão ganha uma especial importância, quer em termos do prognóstico e modelação da evolução futura desses mecanismos de degradação, como no apoio à a priorização das intervenções de manutenção e de reparação a implementar. Neste artigo após uma contextualização dos tipos de degradação do betão relacionados com as reações expansivas internas e a corrosão das armaduras, são apresentadas as principais técnicas de ensaio usadas para o seu diagnóstico, com a exemplificação da sua aplicação a casos concretos, realçando-se os cuidados a ter na interpretação dos resultados.

As argamassas de terra estão presentes nalguns mercados da construção devido a inúmeras vantagens, nomeadamente económicas e ecológicas. Portugal tem um vasto património de construção com terra, sendo estas argamassas as mais adequadas para a sua reabilitação e conservação. No entanto, embora tenham sido realizados alguns estudos sobre o comportamento deste tipo de argamassas, pouco é conhecido sobre a sua durabilidade quando aplicadas no exterior. O objectivo deste estudo é avaliar a influência da adição de baixas quantidades de cais (aérea ou hidráulica natural) e da lavagem da areia na durabilidade de argamassas à base de terra aplicadas como reboco de paredes exteriores. Os resultados obtidos não evidenciam melhoria das características mecânicas e físicas dos rebocos de argamassa de terra com estas adições e lavagem. Assim, para melhorar o desempenho deste material, nomeadamente face à água no estado liquido, recomenda-se o estudo de outras adições, adjuvantes ou protecções de superfície.

Surface consolidation is a common practice in the conservation of the built heritage. However, the effectiveness of consolidation of calcareous materials is often doubtful, due to the lack of effective and compatible consolidation products. Dispersions of calcium hydroxide nanoparticles in alcohol, the so-called nanolimes, can recover the superficial consolidation of calcareous substrates. Nevertheless, they are often not able to guarantee an in-depth consolidation. Previous research by the authors has demonstrated that the effectiveness of nanolime can be improved by fine-tuning the properties and the application protocol of the dispersions, based on the moisture transport properties of the material to be treated. In this paper, we verify the consolidation effectiveness and physical compatibility of the developed nanolimes, when applied on coarse porous calcareous materials like Maastricht limestone and lime-based mortars. The results show that a suitable mass consolidation can be achieved with nanolimes, while maintaining a good compatibility with the substrate material.

The homogeneous state of the concrete in the fresh state has consequences on their properties in the hardened state. The use of pozzolanic concrete must be carefully evaluated, because the physical and chemical differences of each pozzolan have consequences on concrete hardened state properties. In this work, two physical and chemically different pozzolans were used to evaluate the effect on concrete microstructure and its basic hardened state properties. Scanning electron microscopy (SEM) was used and can be an effective tool in the analysis of the microstructure allowing a better understanding of the properties of concrete in hardened state. It allows showing that the differences in the two pozzolans (metakaolin and diatomite) promote different microstructures as well as different final properties of pozzolanic concrete. Moreover, it was also shown that the use of a water reducing agent, to adjust workability instead of water, promotes an improvement in both the microstructure and the hardened state features such as porosity and mechanical strength.

Several concrete structures show signs of deterioration resulting from internal chemical reactions, such as the alkali-silica reaction (ASR). It is well known that these swelling reactions occur in the presence of moisture, between some silica mineral phases present in the aggregates and the alkalis of the concrete, leading to the degradation of concrete structures and consequently compromising their safety. In most of the cases, rehabilitation, demolition or even rebuilding of such structures is needed and the effective costs can be very high. Volcanic rocks are commonly used as aggregates in concrete, and they are sometimes the only option due to the unavailability of other rock types. These rocks may contain different forms of silica that are deleterious to concrete, such as opal, chalcedony, cristobalite, tridymite and micro- to cryptocrystalline quartz, as well as Si-rich volcanic glass. Volcanic rocks are typically very finegrained and their constituting minerals are usually not distinguished under optical microscopy, thus leading to using complementary methods. The objective of this research is to find the more adequate analytical methods to identify silica phases that might be present in volcanic aggregates and cause ASR. The complementary methods used include X-Ray Diffraction (XRD), mineral acid digestion and Scanning Electron Microscopy with Energy Dispersive X-Ray Spectrometry (SEM/EDS), as well as Electron Probe Micro-Analysis (EPMA).

As the cement content is one of the parameters that control alkali–silica reaction (ASR), this study examined its influence on the expansion of glass mortars. The mortars had volumetric ratio of 1:4 (cement: aggregate) and various aggregate compositions, obtained using replacement ratios of natural sand with waste glass, of 0, 20, 50 and 100%. A volumetric ratio 1:4 was chosen because it is a current composition for cementitious coating mortars. In fact, mortar mixes with increased cement content can lead to erroneous conclusions for in situ mixtures with reactive aggregates. It is concluded that it is feasible to produce glass mortars without deleterious ASR expansion depending on the amount of cement used. For normal cement/ aggregate ratios for coating mortars (1:4, in volume), a CEM II/B-L 32.5 N mortar with glass incorporation has a low ASR risk.

Alkali-silica reaction (ASR) is a type of deterioration that has been causing serious expansion, cracking and durability/operational issues in concrete structures worldwide. The presence of sufficient moisture, high alkali content in the cement paste and reactive forms of silica in the aggregates are the required conditions for this reaction to occur. Reactive aggregates of volcanic nature have been reported in different countries such as Japan, Iceland and Turkey, among others. The presence of silica minerals and SiO2-rich volcanic glass is regarded as the main cause for the reactivity of volcanic rocks. In Portugal, volcanic aggregates are mainly present in Azores and Madeira Archipelagos and, for several years, there was no information regarding the potential alkali-reactivity of these rocks. Since the beginning of this decade some data was obtained by the work of Medeiros (2011) and Ramos (2013) and by the national research projects ReAVA, (Characterization of potential reactivity of the volcanic aggregates from the Azores Archipelago: implications on the durability of concrete structures) and IMPROVE (Improvement of performance of aggregates in the inhibition of alkali-aggregate reactions in concrete), respectively. In order to investigate the potential alkali-reactivity of aggregates from both archipelagos, a total of sixteen aggregates were examined under the optical microscope and, some of them, also under the Scanning Electron Microscope with Energy Dispersive X-ray Spectroscopy. A set of geochemical analyses and laboratory expansion tests were also performed on those volcanic aggregates. The main results showed that the presence of volcanic glass is rare in both archipelagos and that the samples of Madeira Archipelago contain clay minerals (mainly from scoria/tuff formations inter-layered with the lava flows), which can play a role in concrete expansion. The results of the laboratory tests showed that one of the samples performed as potentially reactive in the accelerated mortar-bar test (ASTM C 1260) and that the majority of the Azores samples started to show some expansion just after one year of testing in the concrete prism test (CPT) at 38ºC.

Nesta comunicação apresentam-se desenvolvimentos recentes na caracterização mecânica de materiais de construção por técnicas de micro e nanoindentação.

Nesta comunicação apresentam-se desenvolvimentos recentes na caracterização mecânica de materiais de construção por técnicas de micro e nanoindentação.

utilizados na preparação das argamassas. Nos últimos anos, a importância da seleção do tipo de agregados e o seu efeito na alteração das propriedades dos betões e das argamassas tornaram-se amplamente reconhecidos. Estes fatores são particularmente importantes no contexto da reabilitação, com revestimentos com base em cal, uma vez que se pretende utilizar argamassas com características específicas e desempenhos compatíveis com as existentes nas alvenarias antigas. Os agregados, ao serem o constituinte maioritário, assumem um papel fundamental no comportamento físico, químico e mecânico das argamassas, assim como no acabamento e no aspeto final dos rebocos, principalmente no caso das argamassas de cal. A forma e a distribuição granulométrica das areias têm influência, fundamentalmente, na microestrutura das argamassas, que se reflete nas características mecânicas e hígricas, enquanto a natureza mineralógica tem influência sobretudo nas propriedades mecânicas e na durabilidade das argamassas. Na presente comunicação, é analisada a influência da natureza mineralógica dos agregados na estrutura e no comportamento físico-mecânico a longo prazo das argamassas de cal para revestimentos de paredes.

Although considerable efforts have been made worldwide regarding alkali-silica reaction (ASR) prevention and mitigation, including the approval of new national and international regulations, several concrete structures are still being diagnosed with ASR. In Portugal, the new cases of ASR pertain to concrete produced mainly with igneous aggregates, whose potential reactivity is difficult to assess, notably on granitic and basaltic rocks. The most effective way to prevent ASR is an adequate knowledge of the alkali reactivity of the aggregate, which requires the application of appropriate tests and criteria to enable a correct classification. In the last 4 years a research program conducted in Portugal has evaluated more than 90 aggregates of different mineralogy and/or texture. The test campaign included petrography, ASTM C1260, RILEM AAR-3 and RILEM AAR-4.1 test methods. In this paper the results of ASR reactivity evaluation obtained in a group of granitic and basaltic aggregates are presented and discussed. From the results obtained, proposals to improve the reliability of existing test-methods are presented.

Nos últimos anos vários casos de degradação prematura de estruturas de betão têm sido relacionados com a reação sulfática interna (RSI). Esta forma de degradação está relacionada com a remobilização dos sulfatos incluídos na matriz de cimento, devido ao aquecimento excessivo do betão durante as idades iniciais, que conduzem à formação de etringite expansiva (também conhecida por delayed ettringite formation - DEF). Verifica-se que a DEF aparece em betões expostos a humidade frequente e que foram submetidos a um tratamento térmico (T> 65 °C) ou terão atingido temperaturas elevadas por outra razão (elevada dosagem em cimento, peças muito espessas, betonagem durante o verão, etc.). A prevenção da RSI é normalmente efetuada tendo em vista a eliminação de pelo menos um dos fatores que a promovem, nomeadamente pelo controlo da temperatura máxima do betão, dosagem e composição do ligante e humidade. Algumas adições minerais têm a capacidade de reagir com o hidróxido de cálcio da hidratação do cimento, formando compostos hidratados como o silicato de cálcio hidratado, e assim controlar a alcalinidade da solução dos poros do betão, inibindo a formação dos produtos expansivos. No entanto, não há ainda dados suficientes sobre o desempenho a longo prazo dos diferentes tipos de adições. Nesta comunicação apresentam-se e discutem-se os resultados de ensaios de expansão de betão com diferentes tipos de adições minerais (cinzas volantes de carvão, metacaulino, escórias granuladas de alto-forno, sílica fumo, lamas de minas de tungsténio, cinzas de biomassa e fíler calcário) referentes a cerca de 8 anos de acompanhamento, e tecem-se algumas considerações sobre os teores a considerar na prevenção da DEF.

É reconhecido que as intervenções de conservação e restauro do património histórico e arquitetónico deverão começar com uma prévia caracterização dos materiais constituintes (pedra, argamassas, betões, tintas, cerâmicos, metais, madeira, entre outros) e do seu respetivo estado de conservação. Essa caracterização é imprescindível para a elaboração de recomendações relativas ao plano de intervenção e aos materiais e técnicas a aplicar posteriormente. Nos últimos anos o Laboratório Nacional de Engenharia Civil tem coordenado um número considerável de projetos no âmbito da análise histórica e técnica da construção e do respetivo desempenho, bem como nas técnicas e intervenções, detendo um incomparável arquivo de informação sobre a caracterização física, química e mecânica de materiais, processos de deterioração e necessidades de conservação. Neste contexto, surgiu a ideia de agrupar uma equipa interdisciplinar e constituída por especialistas de várias áreas, incluindo químicos, engenheiros, biólogos, entre outros, vindo a envolver, entre outras atividades, a construção de um repositório de materiais históricos, com a compilação de amostras de referência e o desenvolvimento duma aplicação para registo sistematizado de dados relativos à história e às técnicas relacionadas com a aplicação desses materiais, das suas propriedades e, quando possível, do seu desempenho. Esta ideia geral foi também a base do Projeto DB-HERITAGE (refª TDC/EPH-PAT/4684/2014), que conta com o apoio da Fundação para a Ciência e Tecnologia (FCT), e em que participam, para além do LNEC, a NOVA.ID.FCT - Associação para a Inovação e Desenvolvimento da FCT, a Universidade de Aveiro e a Universidade de Évora. Nesta comunicação, apresenta-se o contexto deste projeto e dos principais objetivos a atingir, que visam nomeadamente: a) Disponibilização de um repositório de amostras e dados para estudo e consulta; b) Compilação de informação acerca de materiais de construção utilizados em Portugal ao longo do tempo; c) Descrição do estado de degradação dos materiais de construção, desde que aplicável, considerando o tipo de materiais e respetivas características e o tempo e ambiente de exposição. Estes dados deverão valorizar, através do registo, as atividades técnicas envolvidas no trabalho de conservação de materiais construtivos históricos e espera-se que possam servir de suporte a uma Base de Dados mais global que tenha em conta a intervenção dos Portugueses no Mundo. De referir que este Projeto integra os objetivos da infraestrutura de investigação IPERION-CH.pt, inscrita no Roteiro Nacional de Infraestruturas de Investigação de Interesse Estratégico. Para além da melhoria do conhecimento das características e componentes dos materiais de construção históricos, o projeto DB-HERITAGE permitirá desenvolver formas mais eficientes de utilizar os materiais e os métodos para a sua conservação e restauro, assim contribuindo para a valorização do património.

A corrosão de armaduras no betão armado, por carbonatação do betão ou ataque por iões cloreto, é uma das principais causas de degradação de estruturas. A propagação da corrosão após o seu início é geralmente rápida, podendo conduzir à deterioração das estruturas, num curto espaço de tempo, sempre associada a elevados custos de reparação. A utilização do aço galvanizado é considerada uma medida alternativa para aumentar o tempo de vida útil das estruturas expostas ao ataque de espécies agressivas. Contudo, quando o aço galvanizado é embebido no betão fresco (ambiente extremamente alcalino), a camada de zinco corrói-se durante um certo período até que se forme uma camada de passivação. Em simultâneo, ocorre produção de hidrogénio, originando aumento da porosidade do betão que, por sua vez, pode comprometer a aderência entre o aço e o betão. Para mitigar este processo de corrosão inicial utilizam-se vários procedimentos tais como o aumento do teor de cromatos no cimento ou a deposição de camadas de conversão química à base de crómio (CCC) na superfície do aço galvanizado. No entanto, devido à toxicidade dos iões Cr(VI), os cimentos atualmente comercializados possuem quantidades reduzidas de Cr(VI) e diversas alternativas têm vindo a ser propostas às CCC, nomeadamente camadas de conversão à base de cério, lantânio, zircónio ou molibdénio. Diversos revestimentos à base de resinas epóxi, sílica e silanos foram também estudados bem como revestimentos híbridos obtidos pelo método sol-gel. Neste trabalho serão apresentados e discutidos os resultados mais relevantes de revestimentos e pré-tratamentos alternativos destinados a aços galvanizados publicados no período que decorreu entre 2010 e 2015. A maior percentagem de publicações incidiu nas camadas de conversão química alternativas às de crómio, verificando-se que as camadas de conversão à base de molibdato apresentaram resultados muito promissores e comportamento semelhante às CCC.

Nas últimas décadas tem-se assistido a um grande desenvolvimento de nanomateriais para diversos tipos de aplicações em áreas tão diversas como a energia, eletrónica, biotecnologia, telecomunicações, entre outros. A área da construção não foi excepção e também beneficiou deste desenvolvimento, nomeadamente ao nível dos revestimentos sol-gel para mitigação da corrosão, proteção do património azulejar e de materiais pétreos. O método sol-gel tem sido usado para estes fins, uma vez que possibilita a obtenção de uma vasta gama de revestimentos com propriedades ajustáveis ao fim a que se destinam, e com vantagens ao nível ambiental. Nesta comunicação serão discutidas as aplicações mais relevantes de revestimentos híbridos nanoestruturados sintetizados pelo método sol-gel para mitigação da corrosão na indústria da construção. Será dado maior destaque aos revestimentos híbridos orgânico-inorgânicos desenvolvidos no Laboratório Nacional de Engenharia Civil, estudados para a proteção de armaduras galvanizadas1–3 e de ligas de alumínio4-6, baseados, respetivamente, em ureia-silicatos e amino-álcool-silicatos, e na combinação do 3-Glicidoxipropiltrimetoxisilano com o tetra-n-propóxido de zircónio, aplicados pelo método dip-coating.

O trabalho aqui apresentado insere-se no âmbito de uma tese de doutoramento em curso intitulada: “Identidade da ilha: uma metodologia para estudo e experimento de soluções e valores adotados para conservação e reparação de argamassas de revestimento no centro histórico de São Luís/MA”. São Luís é uma cidade brasileira localizada no estado do Maranhão e detentora de um muito significativo acervo arquitetônico. Inscrito na lista de Patrimônio Mundial da Humanidade da Unesco desde 1997, o centro histórico de São Luís preserva um conjunto aproximado de 5.600 imóveis classificados que apresentam, em muitos casos, um estado de conservação deficitário. Ao realizar um estudo mais pormenorizado da argamassa existente em edifícios do século XIX de São Luís, tornou-se perceptível a qualidade do material do ponto de vista das características físicomecânicas e químicas, assim como a variedade de cores encontradas. Essa constatação acabou por levantar questões arquitetônicas e materiais relacionadas com as influências climáticas e espaciais sobre os edifícios em análise, assim como com os problemas patológicos apresentados nos seus revestimentos, em especial nas argamassas antigas. Propõe-se evidenciar, a partir de 5 edificações selecionadas com base no ano de construção e na localização dentro da malha urbana do centro histórico, a diversidade e as semelhanças encontradas em argamassas desses edifícios ao nível das características, físicas, mecânicas e químicas, relacionando-as com o local de extração e coleta, a incidência de fatores externos, a composição e o estado de conservação. O objetivo final do estudo é reunir os principais dados obtidos, sublinhá-los e discuti-los dentro da realidade na qual se encontram, tendo como ponto relevante a constatação das anomalias existentes, as suas causas e o estado atual de degradação. Estes dados, e a respetiva análise, contribuirão para a definição de futuras soluções de reabilitação e reparo dos revestimentos analisados e discutidos na tese de doutoramento em desenvolvimento.

Alkaline minerals, like feldspars and micas, present in aggregates can release alkalis with time for concrete pore solution, being a contributor factor for the delaying ASR occurrence in some concrete structures (e.g. dams). Since there is presently no consensus on how to test for releasable alkalis in aggregates, a research program has been conducted to evaluate the factors that can affect the alkalis release in laboratory test conditions. This paper presents the results after 455 days evaluation of alkalis released by igneous aggregates with different grain sizes, in different alkaline solutions (Ca(OH)2, NaOH and KOH), in two different concentrations (1M and 0.7M) -with and without addition of saturated Ca(OH)2. The results obtained show that reducing the particle size of the aggregates leads to an increase of alkalis release to the solution, which is higher in the alkaline solutions of KOH and NaOH with saturated Ca(OH)2. The sodium extraction is higher in 0.7M KOH, while potassium is higher in 1M NaOH.

Os artigos que compõem esta edição foram criteriosamente selecionados e aprimorados, seguindo igual metodologia de trabalho do número anterior, contribuindo para compor um dossier temático de elevado interesse e qualidade. No seu conjunto, os vários textos sublinham o papel dos materiais históricos na construção multidimensional do território humanizado, ligando os aspetos tangíveis e intangíveis, transportando saber e gosto, tradição e inovação. Estes artigos, bem como os do primeiro volume, são também uma fonte reflexão e de conhecimento sobre alguns dos materiais de construção mais empregues no Património abrindo, nalguns casos, novas perspetivas para futuras investigações nesta área do conhecimento.

Vários

The use of gypsum plaster for the interior coating of walls and ceilings in the Portuguese architecture was particularly expressive in the period between the XVIII and the XX century. However, information about this important heritage is almost nonexistent, which is leading to a rapid loss of important patrimony. In this paper the results of the characterisation of five gypsum plaster samples from the second half of the XIX century belonging to the Arabian Room of the Bolsa Palace, located in Oporto, North of Portugal, are presented and discussed. XRD and TGA-DTA techniques were used to establish the mineralogical composition, and the relative proportions of the binders. Optical microscopy and FESEM-EDS observations were performed both in fractured and polished surfaces in order to determine the stratigraphy and the composition of individual layers. The results of this characterisation work showed that the plasters used were mainly composed of gypsum and hydrated lime in different proportions – a feature that was correlated with the application techniques of the decorative elements analyzed - and allowed the determining of the restoration interventions they had already been submitted to. Some physical properties like the dynamic modulus of elasticity and capillary absorption were also determined, and a correlation between the results obtained was established with previous studies performed by the authors.

The Santíssimo Sacramento Convent in the Alcântara quarter of Lisbon is one of the most important ecclesiastical structures of the Filipino Period (1580- 1640), showing an innovative architectural layout. An intervention aiming at the repair and restoration of the interior plasters of the Santíssimo Sacramento Church was performed in 2009 and 2010. To support the restoration plan, a physical, mechanical and chemical-mineralogical characterization of the internal plasters of the church was carried out. In this paper the main results are presented, such as various types of plasters, mortars, stuccos and pigments; and also the nature of the main anomalies were identified and characterized. The results obtained contributed to the identification of the main decorative programs characterized by the use of different materials and techniques. The mortars are in very good condition, being composed of aerial calcitic lime with quartzitic and basaltic aggregates. The stuccos are comprised by gypsum and non-hydraulic lime, while the decorative layers features lime with some precious pigments, such as ultramarine (lapislazzuli) and gold-foil gildings. The plaster conservation and restoration works were performed with compatible repair materials selected according to the physical-chemical characterization and on the evaluation of the conservation state.

A degradação de estruturas de betão por reacções expansivas internas é uma patologia que, não sendo relativamente recente a nível internacional, tem vindo a manifestar-se duma forma crescente nos últimos anos em Portugal. Esta patologia tem afectado vários tipos de estruturas de betão, algumas de grande importância estratégica, nomeadamente grandes barragens e obras de arte (pontes e viadutos). A título de exemplo referem-se os casos do Viaduto Duarte Pacheco, e as Barragens de Alto-Ceira e Santa Luzia, alguns dos quais obrigaram a intervenções de elevado custo. Esta forma de degradação, que engloba a reacção álcalis-sílica (RAS) e a reacção sulfática interna (RSI), quando ocorre numa estrutura é particularmente nefasta porque está relacionada com a formação de compostos expansivos que provocam a fissuração do betão, contribuindo decisivamente para a diminuição da vida útil da estrutura, podendo em alguns casos obrigar à sua demolição. Associada a esta situação, acresce o facto de não se dispor actualmente dum método totalmente eficiente e económico de combater esta forma de degradação. Deste modo, para garantir os tempos de vida útil preconizados para as novas construções devemse adoptar medidas preventivas para evitar ou minimizar os efeitos da ocorrência deste tipo de reacções expansivas nas estruturas de betão. Em Portugal, medidas preventivas destas reacções expansivas internas estão contidas na Especificação LNEC E 461, citada na NP EN 206-1 – Betão. Parte 1: Desempenho, especificação, produção e conformidade, a qual inclui a fixação de níveis de prevenção de acordo com a categoria de risco e exposição ambiental do elemento ou da estrutura de betão. Estas medidas passam por uma caracterização dos factores condicionantes destas reacções nos constituintes do betão e pela aplicação de medidas para a sua inibição. Neste particular, a utilização de adições minerais em substituição parcial do clínquer portland, é uma medida que além de diminuir o calor de hidratação, permite a redução da alcalinidade da solução intersticial do betão e contribui ainda para reduzir a quantidade de sulfatos no betão, evitando assim a formação de produtos expansivos. Actualmente é já conhecido que as adições minerais do tipo II, em substituição parcial do cimento no betão e em quantidade suficiente, podem mitigar os efeitos destas reacções. A acção destas adições minerais depende, no entanto, da sua composição e reactividade pozolânica.Apesar dos bons resultados já demonstrados por algumas adições, nomeadamente as cinzas volantes, o seu uso pode estar comprometido a curto/médio prazo, tendo em conta a cada vez maior preocupação, por parte da maioria dos Países, na utilização de renergias “limpas”. Esta tendência terá como consequência uma diminuiçãtt ou mesmo o esgotamento da produção de alguns subprodutos industriais. No caso dos produtos naturais, é previsível um agravamento das restrições ambientais associadas à sua exploração e tratamento. Foi neste contexto que se iniciou no LNEC, em colaboração com o Laboratoire Central des Ponts et Chaussées de Paris e as Universidades de Aveiro, Minho e Évora, um projecto de avaliação da utilização de novos materiais com características pozolânicas, capazes de responderem às necessidades da indústria do betão a curto/médio prazo. Este projecto, que contou com o apoio da Fundação para a Ciência e Tecnologia (Projecto PTDC/CTM/65243/2006 – EXREACT – Mitigação de reacções expansivas deletérias em estruturas de betão) visa ainda o aperfeiçoamento de metodologias de diagnóstico e prognóstico da ocorrência de reacções expansivas internas em estruturas de betão existentes. Os resultados do trabalho realizado no decorrer do projecto têm vindo a ser divulgados em artigos e comunicações em seminários nacionais e internacionais, mas também através duma página Web (http://www-ext.lnec.pt/EXREACT/index.html) e com a organização de reuniões como a do presente Workshop, que contou com o apoio do LNEC, da Comissão Organizadora do REABILITAR 2010 - Encontro Nacional de Conservação e Reabilitação de Estruturas e dos oradores convidados. Este Workshop visa apresentar os últimos desenvolvimentos sobre os aspectos da prevenção, modelação e reparação, proporcionando uma oportunidade para a compartilha de ideias e soluções para a gestão das estruturas afectadas por RAS e/ou RSI.

The growing interest in preserving the built heritage is a driving force towards the search for new rehabilitation solutions compatible with the original construction techniques of ancient buildings. For the design of an adequate reinforcement solution, it is necessary to know in detail the building to be rehabilitated, as well as its original constructive solutions and materials.This paper presents the results of an experimental campaign on samples of air lime-based laying and coating mortars, extracted from an old masonry building in the historic center of Lisbon, built in 1910, during the rehabilitation works. The different parameters analyzed allow for the composition characterization and evaluation of their mechanical, physical and chemical properties. Based on this characterization, the influence of these mortars on the overall behavior of load-bearing walls of buildings belonging to the typology under study is also evaluated.Considering the results obtained in the characterization tests for the mortars in study, it was verified that the binder used in both mortars was air lime. The values for compressive strength, modulus of elasticity and the curves obtained in the capillarity and drying tests, are also compatible with this type of mortars. It was determined that the mortars are similar in terms of physical and mechanical characteristics, to Portuguese mortars studied in current buildings of the same historical period. This type of information is crucial in a structural analysis and allows to identify materials compatible with the original ones that can be used in rehabilitation interventions.

Cementitious materials have a considerable global warming footprint. This is due mainly tothe cement incorporated. For a tonne of cement produced other 800 kg of CO2 [1] are releasedinto the atmosphere.According to the European Sustainable Development Goals, cement industry should becomecarbon neutral by 2050. To meet this goal, the European Cement Association (Cembureau)developed a Roadmap with specific guidelines by 2050 based on five approaches (5C). Thefirst four are focused on improvements in clinker production, cement formulation,construction processes and concrete formulations. The last 5C is re-carbonation of thecementitious materials.This research investigates the CO2 absorption capability of recycled aggregates (RA) fromconstruction and demolition wastes (CDW), when submitted to a forced carbonation. It isknown that CDW still have some potential to CO2 capture, which is a long-term and securecarbon storage. For that purpose, several CDW were collected from recycling plants, fromselective demolitions and from concrete plants.It was concluded that RA when submitted to forced carbonation absorb between 47 to 315 kgof CO2 per tonne of cement paste, which has a potential to meet the re-carbonation targetsestablished by the roadmaps to carbon neutrality.

The Mirante da Quinta da Azeda, in Setúbal (Portugal), is a peculiar observation tower built in the early 20th century, and one of the first examples in which reinforced concrete was applied in Portugal. It has an unusual architectural configuration, displaying elements of great slenderness. In the scope of the CemRestore research project - Mortars for the conservation of early 20th century buildings: compatibility and sustainability, several mortar and concrete samples were collected from this structure and were characterized using a combination of mineralogical, microstructural, physical, and mechanical techniques, including XRD, petrography, SEM-EDS, open porosity, capillarity coefficient, compressive strength, and ultrasonic pulse testing. In this paper, the main characterization results are presented and discussed. The results show that all structural and decorative samples are made with Portland cement, while one rendering mortar is lime-based. The sand is mostly siliceous whereas pebbles and crushed limestone can be found as coarse aggregates in concrete samples. This characterization allows for broadening the scientific knowledge about the materials of that period used in Portugal, also enabling the establishment of the requirements to be met by mortars and concrete to be used in the repair of this distinct structure.

Earth mortars and gypsum mortars present ecological advantages compared to mortars made with other common binders. When applied as plasters, they are also referred as having advantages in improving comfort and indoor air quality. For earth plasters, this improvement is associated with the hygroscopic capacity of the clay minerals, which promotes high sorption and desorption capacity of water vapor. So, earth plasters can contribute to the regulation of the indoor relative humidity. Another important advantage of plasters could be their ability to capture carbon dioxide (CO2). In the present study, the sorption and desorption performance, and the capacity to capture CO2 by earth and gypsum plasters are evaluated. It is confirmed that the earth plaster has the greatest sorption and desorption capacity, but also higher CO2 capture capacity than gypsum plaster. This confirmation opens new perspectives for the use of functionalized plasters that guarantee greater control of air quality inside buildings.

Coimbra apresenta um elevado valor arquitetónico demonstrado pelos 36 imóveis, conjuntos ou sítios (22 monumentos nacionais e 14 imóveis de interesse público) actualmente classificados (DGPC, 2015) sendo a maioria deles localizados no Centro Histórico de Coimbra (CHC) e zona alta da cidade. No âmbito do projecto POCI/HEC/60371/2004 ‘Bases para o restauro dos revestimentos históricos do Centro Histórico de Coimbra’, foi feito um levantamento das existências cromáticas existentes no CHC-Alta (zona de edifícios de habitação da Alta de Coimbra, Figura 3.1), a partir do qual se seleccionaram edifícios que ainda apresentavam vestígios de pinturas em várias camadas, o mais antigas possível.

Os revestimentos híbridos nanoestruturados apresentam um elevado potencial no âmbito da protecção anticorrosiva dos metais, prevendo-se que no futuro estes revestimentos possam, não só substituir os tratamentos à base de crómio usados na indústria do tratamento de superfícies metálicas para protecção anticorrosiva, como também evoluir para sistemas integrados multifuncionais que dispensem o pré-tratamento e sejam mais “amigos” do ambiente. O processo sol-gel usado para a obtenção destes revestimentos permite, através da combinação de diferentes precursores e da manipulação das condições de síntese “desenhar” e optimizar a estrutura química e a funcionalidade dos revestimentos nanoestruturados com o objectivo de obter as propriedades desejadas para uma determinada aplicação. O estudo apresentado no presente trabalho teve como objectivo principal a optimização de revestimentos híbridos nanoestruturados obtidos pelo processo sol-gel para a protecção anticorrosiva de uma liga de alumínio frequentemente utilizada na construção civil. Para alcançar este objectivo foram preparados diversos revestimentos híbridos nanoestruturados e aplicados na liga de alumínio EN AW-6063, cujo processo de síntese foi optimizado variando parâmetros como a composição, processo de cura e condições reaccionais sol-gel, visando a obtenção de revestimentos com propriedades anticorrosivas melhoradas. Posteriormente, foi feita uma avaliação do comportamento à corrosão dos revestimentos optimizados em diferentes condições corrosivas, individualmente e como parte integrante de um sistema de protecção anticorrosiva usualmente aplicado em ligas de alumínio para fins arquitecturais. No presente documento é apresentada uma revisão bibliográfica da aplicação deste tipo de revestimentos na protecção anticorrosiva, seguindo-se a descrição detalhada dos procedimentos experimentais do estudo, nomeadamente, os materiais e os procedimentos para obtenção e caracterização dos revestimentos estudados, a apresentação dos resultados obtidos no decurso do desenvolvimento experimental realizado, sua interpretação, discussão e as conclusões parciais mais relevantes. No final, resumem-se as principais conclusões obtidas no estudo e faz-se uma avaliação global da aplicabilidade dos revestimentos optimizados na protecção anticorrosiva de ligas de alumínio no âmbito da construção civil, e indicam-se necessidades de desenvolvimentos futuros.

Nesta dissertação, estudou-se o comportamento electroquímico de cinco ligas austeníticas de aço inoxidável em meio alcalino, nomeadamente duas ligas de Fe-Cr-Ni (1.4301?SS0 e 1.4436?SS4) e três novas ligas de elevado teor em manganês Fe-Cr-Mn (SS1, SS2 e SS3). Os estudos incidiram na avaliação da resistência à corrosão das ligas, em soluções alcalinas e no betão, e na caracterização das propriedades dos filmes de passivação sob influências várias, designadamente, condições de estabilização (electrólito, tempo e potencial de formação do filme), composição e microestrutura das ligas, soldadura e estado da superfície do aço. O estudo da capacidade diferencial em função do potencial mostra o comportamento dos filmes de passivação como semicondutores tipo-n e tipo-p, respectivamente, para valores anódicos e catódicos relativamente aos potenciais de banda plana, possibilitando a determinação das suas propriedades electrónicas. Estas traduzem as principais diferenças dos dois grupos de ligas, sendo que as ligas de Fe-Cr-Mn mostram uma menor razão da densidade de aceitadores com a densidade total de portadores de carga, do que as ligas de Fe-Cr-Ni, e um nível de doadores profundo, cuja ionização depende do potencial aplicado. Todas as ligas revelaram uma elevada resistência à corrosão nos diferentes meios, sendo a sua estabilidade especialmente dependente do acabamento superficial do aço e da existência de condições que promovam a corrosão intersticial. A soldadura das ligas induziu a formação de picadas instáveis, cuja repassivação foi desfavorecida em duas das ligas de Fe-Cr-Mn (SS1 e SS3). A presença de fissuras no betão demonstrou a despassivação das ligas e a susceptibilidade à corrosão sob tensão da liga SS1 no betão. As propriedades dos filmes de passivação, nomeadamente as densidades dos portadores de carga, que podem ser correlacionadas com a composição e a microestrutura das ligas, justificam as diferenças no comportamento electroquímico das ligas de Fe-Cr-Ni e de Fe-Cr-Mn. Para além das diferenças promovidas pelos teores de níquel e de manganês e pela ferrite, a maior resistência à corrosão das ligas SS2 e SS4, respectivamente, quando comparadas com as restantes ligas de Fe-Cr-Ni (SS0) e Fe-Cr-Mn (SS1 e SS3), é devida à presença do molibdénio e seus eventuais efeitos sinergéticos com o crómio e azoto.

O estudo da composição de argamassas antigas, que implica usualmente a utilização de técnicas de caracterização físico-química, mineralógica e microestrutural, desempenha um papel fundamental para a preservação do património cultural, permitindo obter um conhecimento bastante profundo sobre os seus constituintes e revelando detalhes importantes sobre as técnicas de construção, eventuais reparações e o estado de conservação e desempenho das mesmas. Neste trabalho foram analisadas argamassas provenientes de quatro edifícios religiosos da região do Alentejo, nomeadamente a Sé Catedral de Évora (Séc. XIII-XVII), a Igreja de Nossa Senhora da Assunção em Elvas (Séc. XVI), a Igreja Matriz de Mértola (Séc. XII) e o Conjunto Monumental de Amieira do Tejo (Séc. XIV-XVI). A metodologia de caracterização empregue recorreu a diversas técnicas, nomeadamente difracção de raios X (DRX), análise termogravimétrica (ATG), microscopia óptica (MO), microscopia electrónica de varrimento acoplada a espectroscopia de raios X por dispersão de energias (MEV-EDS), espectrofotometria de absorção atómica (EAA), potenciometria, gravimetria, sorção de água por capilaridade, resistência mecânica, porosimetria de mercúrio e a adsorção de azoto a – 196 ºC. A aplicação da metodologia proposta permitiu determinar a composição e o estado de conservação das diversas argamassas, tendo-se constatado que nas argamassas da Sé Catedral de Évora e da antiga Sé de Elvas foram utilizados dois tipos de ligantes aéreos, cal calcítica e cal dolomítica, sendo o primeiro tipo o predominante. Nos casos de estudo da Igreja Matriz de Mértola e do Conjunto Monumental de Amieira do Tejo, as argamassas apresentam um ligante essencialmente calcítico. Verificou-se que os agregados utilizados são correlacionáveis com a litologia local de cada caso de estudo. As argamassas apresentam diferentes proporções de agregado, e nos casos de estudo da Sé Catedral de Évora, antiga Sé de Elvas e Igreja Matriz de Mértola foram utilizados fragmentos cerâmicos como aditivos.

Os fenómenos de instabilidade de taludes são frequentemente causa de acidentes humanos e materiais constituindo por esse motivo um problema geotécnico de maior importância. Os estudos dos movimentos de terra, são relativamente morosos e complexos, uma vez que é necessário ter em atenção muitos factores, quer relacionados com características internas ao maciço, ou seja, características geológicas e geotécnicas, quer com acções externas. Os estudos das instabilidades de taludes ou vertentes naturais, têm como objectivo avaliar avaliar a perigosidade associada à sua ocorrência, os correspondentes riscos e definir medidas de prevenção e de controlo dos movimentos de terra que possam ocorrer. As modificações geológicas e climáticas experimentadas ao longo do tempo geram uma modificação constante na geometria dos taludes devido à sua sucessiva adaptação a novas condições de equilíbrio. Geralmente, as áreas mais propícias à ocorrência deste tipo de movimentos, correspondem a zonas montanhosas, escarpadas e sujeitas a elevada precipitação ou a condições hidrogeológicas desfavoráveis. Deste modo, a presente dissertação tem por objectivo fazer uma abordagem da problemática associada à instabilidade de taludes em rochas silto-argilosas, dando uma panorâmica das técnicas de engenharia usadas para o controlo dessas situações e salientando-se algumas técnicas de biorremediação apropriadas para o controlo de movimentos superficiais. Os temas abordados são explicados com uma aplicação a um caso real de estudo em Portugal.

N/A

N/A

N/A

A presente comunicação descreve alguns resultados da primeira fase de um trabalho experimental sobre as reacções álcalis-sílica (RAS) em betões com agregados reciclados (BAR). As RAS surgem no betão com agregados convencionais (BAC) devido à combinação de sílica reactiva, álcalis e humidade em quantidades suficientes. Nestas condições, ao longo do tempo, desenvolve-se um gel expansivo que provoca a degradação das estruturas com redução da sua durabilidade. A possível ocorrência das RAS nos BAR serviu de motivação aos autores para o desenvolvimento de um estudo relativo à análise destas reacções em betões com incorporação total e parcial de agregados recicla-dos (AR). Serão analisadas em particular variações no grau de reactividade aos álcalis, no tipo de cimento e de cura empregues tendo em vista verificar se a incorporação de AR nos betões torna ou não mais dano-sa a problemática da RAS, comparativamente aos BAC. Descrevem-se também nesta comunicação alguns aspectos, observados na bibliografia, de diferenças entre a análise das RAS nos BAR e nos BAC.

N/A

In this report, results of a study carried out with the objective of establishing the conditions for artificial weathering practice adequate to patinated bronze with applied conservation treatments are presented. The work developed is part of the research activities that have been carried out in the Metallic Materials Division for the European project ARTECH, integrated in the working group JRA1: Development and evaluation of new treatments for the conservation-restoration of outdoor stone and bronze monuments.

O presente trabalho insere-se no estudo “Desenvolvimento de métodos de caracterização química e microestrutural e de diagnóstico da patologia dos materiais”, Procº 0204/11/16163, incluído no projecto de investigação programada do LNEC para 2005 – 2008 “Qualidade dos Materiais”. Foram analisadas amostras de revestimentos exteriores provenientes do Palácio do Lidador em Beja, que foram disponibilizadas na sequência de trabalhos empreendidos pela Câmara Municipal de Beja que contemplaram a recuperação, consolidação e preenchimento de lacunas e reintegração cromática dos revestimentos e acabamentos exteriores do edifício. O trabalho consistiu na caracterização de cinco revestimentos exteriores, nomeadamente com a realização de análises estratigráficas de todas as amostras e de análise química, mineralógica e microestrutural [1] das argamassas de duas das amostras. Neste Relatório incluiu-se a descrição das amostras e o modo de preparação para os ensaios, apresentam-se os resultados obtidos e faz-se a sua apreciação.

Nos últimos anos tem-se verificado um aumento do número de casos de estruturas de betão afectadas por reacções químicas expansivas de origem interna, nomeadamente pela reacção sulfática interna (RSI), que se caracteriza pela formação de etringite expansiva, em particular a que está associada com a formação de etringite retardada (DEF). Esta reacção é muito difícil de combater, não existindo actualmente um método eficaz de reparação de estruturas degradas por RSI. Tendo em conta este facto, existe uma necessidade premente de encontrar métodos preventivos que possibilitem a inibição da formação de DEF em novas construções. A primeira parte deste trabalho apresenta os resultados de um estudo a longo prazo sobre a influência das cinzas volantes e do metacaulino no desenvolvimento da RSI, em particular na inibição da formação da DEF. Para tal, betões com diferentes razões água/cimento (A/C) e tipo de brita foram produzidos e sujeitos a tratamento térmico. Medidas de expansão dos vários betões foram efectuadas durante um período de 1000 dias após o que se procedeu à sua caracterização microestrutural por MEV/EDS. Os resultados mostram que tanto as cinzas volantes como o metacaulino parecem inibir a RSI, e que a natureza mineralógica dos agregados igualmente desempenha um papel importante na reacção bem como a razão A/C. Face a estes resultados, foi programada a segunda parte do trabalho com o objectivo de determinar a quantidade mínima a partir da qual a presença de adição inibe a DEF. Foi ainda testado também um outro tipo de adição – filer calcário. Para tal, betões de agregado silicioso com menores percentagens de adição foram produzidos em condições idênticas às da primeira parte do trabalho. Os resultados obtidos parecem mostrar que o mecanismo de inibição da RSI é semelhante para o metacaulino e cinzas volantes, e que 10% de metacaulino ou 15% de cinzas volantes parece ser suficiente para inibir a DEF, enquanto que o filer calcário não parece inibir esta reacção expansiva.

No âmbito do projecto financiado pela FCT (Projecto CATHEDRAL – Caracterização e Conservação de Argamassas Tradicionais e Históricas de Edifícios Religiosos do Alentejo – POCI/HEC/57915/2004), em que participam o Laboratório Nacional de Engenharia Civil (LNEC), a Universidade de Évora e o Instituto Português do Património Arquitectónico (antigo IPPAR) e a Faculdade de Ciências da Universidade de Lisboa (FCUL), a Bolseira de Investigação Patrícia Alexandra Alves Pedro Adriano analisou argamassas provenientes de quatro monumentos do Alentejo e pertencentes a períodos históricos diferentes: a Sé Catedral de Évora (Séc. XIII-XVII), a Igreja de Nossa Senhora da Assunção em Elvas (Séc. XVI), a Igreja Matriz de Mértola (Séc. XII) e o Conjunto Monumental de Amieira do Tejo (Séc. XIV-XVI).

Neste relatório apresentam-se os resultados dos ensaios de envelhecimento natural e artificial de tratamentos para a conservação de bronze patinado, realizados com o objectivo de avaliar a eficácia dos sistemas aplicados. Os produtos de conservação em estudo foram desenvolvidos no âmbito do projecto europeu Eu-ARTECH. O trabalho desenvolvido foi realizado no Núcleo de Materiais Metálicos, durante 2008, no âmbito projecto Eu-ARTECH, inserido no grupo de trabalho JRA1: Development and evaluation of new treatments for the conservation-restoration of outdoor stone and bronze monuments.

The organic-inorganic hybrid sol-gel films have been reported as an effective anti-corrosion and environmentally friendly alternative to Cr(VI) pre-treatment for aluminium alloys. These hybrid materials, constituted by nanostructured polymer networks, interconnecting organic and inorganic materials, are of interest because the synergic effect on the mechanical and chemical properties achieved. The organic components impart flexibility, density and functional compatibility with organic coatings, while inorganic components impart hardness, resistance to abrasion and improve adhesion to the metal substrate. The sol-gel process used to obtain these coatings, through a series of simultaneous hydrolysis and condensations reactions between alkoxide precursors, yields highly adherent, chemically inert films on metal substrates and allows the variation of the different synthesis parameters to achieve coatings with optimized properties. In this work, hybrid films were synthesized from glycidoxypropyltrimethoxysilane (GPTMS) and zirconium n-propoxide (TPOZ) precursors, using different amounts of TPOZ (10%, 20%, 30%) and applied to EN AW-6063 alloy by dip-coating, aiming to achieve the best anticorrosive coating. The corrosion behaviour of aluminium specimens coated with these films was evaluated by Electrochemical Impedance Spectroscopy (EIS) in 0.5 M NaCl solution for 63 days. The results obtained revealed that the hybrid films provided effective corrosion protection, exhibiting good barrier properties, however, it was found that 30% of TPOZ led to a marked decrease in the barrier properties with time. The hybrid films prepared were also characterized by Energy Dispersive Spectroscopy (EDS), Scanning Electron Microscopy (SEM), Infrared Spectroscopy and Thermogravimetric Analysis (TGA-DTG) in order to relate their morphology and chemical structure with the corrosion behaviour.

The general designation of “internal expansive reactions” includes the alkali-silica reaction (ASR) and the internal sulfate attack by delayed ettringite formation (DEF). These reactions are characterized by the formation of expansive compounds in hardened concrete and consequent cracking of the structure. In Portugal, the number of structures, mainly dams and bridges, affected by ASR is very significant and in some cases require considerable investment in rehabilitation interventions. Moreover, previous research has shown that the use of some aggregates, initially regarded as inert, can cause problems, proving the need for further insight on the role of aggregates and prevent the occurrence of ASR in constructions. The economic value of various types of structures (e.g. dams, bridges, airfields) and the high costs related to structural degradation including losses of functionality and the permanent or temporary unavailability (for repair and rehabilitation) could be an important overthrow. Thus thorough understanding of the earth materials requirements for concrete manufacture are of vital economic importance in view of the prevention of deterioration and aging of structures whose longevity and functionality must be guaranteed. It is imperative to provide the concrete producers with the necessary knowledge in order to avoid this type of concrete degradation. Particularly important is the recently approved Lisbon-Madrid High Speed Train railway construction. This expensive operation will require large quantities of aggregates for the construction of bridges and other concrete infrastructures. Three main sources of raw materials will be considered for the study: St. Eulalia, Montemor and Cano. These quarries are already major exploitation sites separated by 50 km and not far from the future High Speed Train railway. Two of them are granitoid rocks but the raw material from St. Eulalia is richer in quartz and poorer in ferromagnesian minerals than the Montemor aggregates. The enrichment in calcium of feldspar goes together with the iron and the magnesium. The Cano aggregates are very different materials. The main lithology is a dolomite rock with local microscopic enrichments in phyllosilicates and very deformed quartz. Mineralogical and textural characterization of the aggregates was done by optical microscopy. The crystallinity of quartz was also evaluated by XRD and FTIR. The aggregates were also studied by accelerated expansion mortar-bar and concrete-prism tests to evaluate their potentially alkali-reactivity. The relationship between aggregates characteristics and their behaviour in what concerns to alkali reactivity will be discussed.